Shihweichieh (talk | contribs) (Created page with "==Preparation of AgNWs solutions== The dispersion of AgNWs was spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remain...") |
Shihweichieh (talk | contribs) m (→Preparation of AgNWs solutions) |
||
Line 1: | Line 1: | ||
==Preparation of AgNWs solutions== | ==Preparation of AgNWs solutions== | ||
− | The dispersion of AgNWs was spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent. | + | The wet slurry AgNWs in diameter <100nm, length >30nm purchased from [https://item.taobao.com/item.htm?spm=a1z09.2.0.0.72f92e8dvw2Bxy&id=633022810999&_u=22f32sdpd457 Taobao supplier] was mixed in IPA solution to a concentration of 0.066 mg mL−1 and sonicated for a further 30 min before use. The dispersion of AgNWs was then spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent. |
Revision as of 12:23, 2 October 2023
Preparation of AgNWs solutions
The wet slurry AgNWs in diameter <100nm, length >30nm purchased from Taobao supplier was mixed in IPA solution to a concentration of 0.066 mg mL−1 and sonicated for a further 30 min before use. The dispersion of AgNWs was then spin-coated (500 rpm for 20 s) onto the glass and heated on a hot plate at 60 °C for 5 min to remove any remaining organic solvent.